Spherical CoCrMo Powder
Formula | CoCrMo |
Synonyms | spherical CoCrMo particles, spherical CoCrMo powders, CoCrMo Powder, CoCrMo thermal spray powder, CoCrMo gas atomized powder |
Appearance | Black Powder |
Particle Size | 15-53 um, 45-105 um, can be customized upon request |
Melting Point | 1427°C |
Density | 8.4 g/cm 3 |
Tensile Strength, Ultimate | 780-1280 MPa |
Tensile Strength, Yield | 480-840 MPa |
Description of Spherical CoCrMo Powder
Spherical CoCrMo powder is a cobalt-chromium-molybdenum alloy known for its exceptional wear resistance, corrosion resistance, and biocompatibility. Produced typically through gas atomization, the powder has spherical particles that offer excellent flowability, making it ideal for additive manufacturing and powder metallurgy.
Princeton Powder is a leading supplier of Spherical CoCrMo powder. We specialize in a comprehensive range of spherical powder products and possess extensive expertise in additive manufacturing (3D printing) industry. Spherical CoCrMo powder is for sale at a competitive price.
Chemical Composition
Chemical Composition (wt%) | ||||||||||
Item | Fe | Co | Mn | Si | Ni | Cr | Mo | W | Be | Cd |
CoCrMo | – | Bal. | – | – | ≤0.02 | 26.1~30.1 | 4.3~6.3 | 4.0~6.0 | ≤0.02 | ≤0.02 |
Oxygen≤500 ppm; Nitrogen≤100 ppm
Particle Size distribution
0-15μm, 15-53μm, 45-105μm, 45-150μm. (Various particle sizes can be customized)
Applications
- Medical Implants: Widely used in orthopedic and dental implants for its durability and biocompatibility.
- Aerospace: Suitable for components requiring high strength and corrosion resistance.
- Additive Manufacturing: Ideal for 3D printing complex, high-performance parts
Spherical CoCrMo Powder reference
Study on Biocompatibility of CoCrMo Alloy Parts Manufactured by Selective Laser Melting
- The biocompatibility of implant is generally believed to be an important factor affecting the operation success and service life of implant, the biocompatibility study of CoCrMo alloy fabricated by selective laser melting (SLM) method thus becomes the key for the successful application of personalized implant. We determined both the blood compatibility and the release rate of ions of SLM-manufactured and cast CoCrMo alloy implants following submersion in various corrosive solutions. The surface structure and morphology of the samples before and after the experiment were investigated to ascertain the mechanisms of ion release and blood compatibility. The results indicated that the concentrations of Co and Cr ions of the SLM-manufactured parts after incubation in the different corrosive liquids were less than that of the cast parts, in which increased roughness presented greater potential for Co ion release compared to surfaces with low roughness.
Cobalt-chromium alloy CoCrMo. Biocompatible metallic printing material made of cobalt-chromium-molybdenum alloy. Finished products made of this material have a very high specific strength, wear resistance and corrosion resistance. Supplied in powder form with a nominal particle size of 15 to 45 microns.